spiekana austenityczna stal nierdzewna, dodatek molibdenu, korozja wżerowa, polaryzacja potencjodynamiczna
Abstrakt
Molybdenum was introduced into sintered austenitic stainless steels to improve their corrosion resistance. The influence of different Mo contents on the pitting corrosion resistance of AISI 304L and 316L steels in 0.1 M sodium chloride solution has been investigated. The corrosion behaviour was evaluated by potentiodynamic polarisation method. Sintered Mo-containing 304L steel is less prone to pitting corrosion in environment containing chlorides than 316L with Mo addition. The introduction of molybdenum to 304L steel resulted in an improvement of corrosion resistance. This steel exhibits the highest value of polarisation resistance as well as the lowest value of corrosion rate.
Molibden wprowadzono do austenitycznych stali nierdzewnych w celu poprawy ich odporności na korozję. Badano wpływ różnej zawartości molibdenu na odporność na korozję wżerową stali AISI 304L i 316L w 0.1 M roztworze chlorku sodu. Zachowanie korozyjne oceniano metodą polaryzacji potencjodynamicznej. Spiekana stal 304L zawierająca molibden jest mniej podatna na korozję wżerową w środowisku zawierającym chlorki niż 316L z dodatkiem Mo. Wprowadzenie molibdenu do stali 304L spowodowało poprawę odporności na korozję. Stal ta wykazuje najwyższą wartość oporu polaryzacji, jak i najniższą wartość szybkości korozji.
Wydział
Wydział Mechaniczny
Licencja
Licencja PK
Prawa dostępu
Zasób dostępny dla wszystkich
Na stronie wykorzystywane są pliki cookie, bądź podobne rozwiązania. Aby poznać szczegóły zapoznaj się z polityką prywatności.