symulacja fizyczna, tomografia komputerowa, wysokie temperatury
Abstrakt
The condition of steel deformation in a semi-solid state should be as isothermal as possible due to the very high sensitivity of material rheology to even small variations of temperature. The basic reason for uneven temperature distribution (melting zone) inside the sample body on the Gleeble thermo-mechanical simulator is the contact with cold/warm copper handles. The semi-solid conditions in central parts of the sample cause even greater temperature gradient due to latent transformation heat. Such non-uniform temperature distribution is the source of significant differences in the microstructure and, hence, in material rheological properties. In the paper example results of tomographic studies were presented for both experimental variants (with warm and cold handles).
Proces odkształcania stali w stanie półciekłym powinien być realizowany w warunkach izotermicznych, w związku z dużą czułością własności mechanicznych na niewielkie zmiany temperatury. Głównym powodem nierównomiernego rozkładu temperatury (kształtu strefy przetopienia) w objętości próbki jest wpływ użytych podczas eksperymentów uchwytów miedzianych, tzw. ciepłych i zimnych. Kolejnym ważnym czynnikiem wpływającym na kształt strefy przetopienia jest generowane ciepło krzepnięcia wpływające także bezpośrednio na kształt strefy przetopienia i właściwości mikrostrukturalne i reologiczne. W prezentowanej pracy przedstawiono przykładowe wyniki analiz tomograficznych dla dwóch próbek, z których każda była przetapiana w innej konfiguracji narzędzi (uchwyty zimne i ciepłe).
Wydział
Zbiory cyfrowe BPK
Licencja
Licencja PK
Prawa dostępu
Zasób dostępny dla wszystkich
Na stronie wykorzystywane są pliki cookie, bądź podobne rozwiązania. Aby poznać szczegóły zapoznaj się z polityką prywatności.