The aim of the paper is to demonstrate and describe the fatigue failure mechanisms of eight-layer glass-epoxy composites with a central circular delamination, numerical description of the delamination problems and a possible optimal design. There are a few variables (tension and compression forces, number of cycles, construction of the tested plates) which can be changed during the experiment that will very likely provide different results. The problem is to find the link among all those variables to fully describe their influence on the physical behavior of the epoxy plate which is the subject of the experiment. The results are illustrated with the use of the numerical analysis method. Thanks to that, it is possible to describe how the number of cycles, tension force and stress variations affect the whole fatigue process.
Celem pracy jest zademonstrowanie i opisanie mechanizmów uszkodzenia zmęczeniowego ośmiowarstwowych kompozytów szkło/żywica epoksydowa z kołową delaminacją. Opierano się na numerycznym opisie problemów z rozwarstwieniem. Brane są pod uwagę różne zmienne (siły rozciągające i ściskające, liczba cykli), którymi można operować podczas eksperymentu, co wpływa na wyniki. Problem polega na znalezieniu powiązania wszystkich tych zmiennych, aby w pełni opisać ich wpływ na fizyczne właściwości płyty, która jest przedmiotem badania. Wyniki są ilustrowane za pomocą metody analizy numerycznej. Dzięki temu możliwe jest opisanie, jak liczba cykli, siła i zmiany naprężeń wpływają na cały proces zmęczeniowy.