The 316L-hydroxyapatite biocomposites were produced by the powder metallurgy technology. The properties and microstructure of these materials are affected by the chemical composition of the powders mixture and the sintering temperature. The sintering temperature of 1240°C and hydroxyapatite addition in an amount of 3% of mass obtained the highest density and hardness and smaller open and closed porosity. Hydroxyapatite addition to austenitic stainless steel modified sintering behaviour. During heating the thermal decomposition of hydroxyapatite took place, which led to the formation of a CaO phase. However, phosphorus diffused into the austenitic matrix and was involved in the eutectic transformation.
Kompozyty 316L-hydroksyapatyt zostały wytworzone technologią metalurgii proszków. Właściwości i mikrostruktura badanych materiałów uzależnione są od składu chemicznego mieszanki proszków oraz zastosowanej temperatury spiekania. Temperatura spiekania 1240°C i dodatek hydroksyapatytu w ilości 3% wag. pozwalają uzyskać najwyższą gęstość i twardość oraz najmniejszą porowatość otwartą i zamkniętą. Hydroksyapatyt wpływa na przebieg procesu spiekania stali austenitycznej. Podczas nagrzewania następuje rozkład hydroksyapatytu, który prowadzi do powstania fazy CaO. Natomiast fosfor dyfunduje do osnowy austenitycznej, a następnie bierze udział w przemianie eutektycznej.
Department
Faculty of Mechanical Engineering
License
Licencja PK
Access rights
Zasób dostępny dla wszystkich
Cookies or other similar solutions are used on the page. Take a look at privacy policy to get to know the details.