The purpose of this article is to present the impact of vanadium substitution on the dielectric properties of barium titanate. Doping barium titanate (BaTiO3) by different ions such as vanadium V5+ provides the possibility of changing its dielectric properties. SEM images indicate the differences between pure BaTiO3 (BT) and Ba(Ti0.98V0.02)O3 (BTV2). Using dielectric measurements, the Curie temperatures (Tc) were calculated – they were found to be equal to 403 K and 396 K, respectively. Moreover, for BTV2 the Curie - Weiss temperature and the Curie constant (C) were determined (T0 = 368 K and C = 1.46 ×105 K, respectively).
Domieszkowanie tytanianu baru BaTiO3 (BT) jonami innych pierwiastków, jak wanad V5+, umożliwia zmiany jego właściwości dielektrycznych. Obserwacje z wykorzystaniem SEM wskazują na różnice w strukturze mikrokrystalicznej między BaTiO3 (BT) a Ba(Ti0.98V0.02)O3 (BTV2). Z pomiarów dielektrycznych wyznaczono temperaturę Curie (Tc). Dla BT wynosi ona 403 K, a dla BTV2 396 K. Dla BTV2 określono również temperaturę Curie-Weissa oraz stałą Curie (T0 = 368 K and C = 1.46 ×105 K).
Klasyfikacja PKT
250000 Chemia
Wydział
Zbiory cyfrowe BPK
Licencja
Licencja PK
Prawa dostępu
Zasób dostępny dla wszystkich
Na stronie wykorzystywane są pliki cookie, bądź podobne rozwiązania. Aby poznać szczegóły zapoznaj się z polityką prywatności.